Biodegradable container

ABSTRACT

A container which deteriorates after a prolonged exposure to moisture and oxygen in an atmospheric environment with the aid of biological agents. The container material has organic components that are nutrients to fungi and various bacteria which bring about the decomposition. The material is composed of an organic filler material, such as peat, and a phenolic resin impregnated with a metallic salt of a fatty acid. The decomposition process transforms the container material into a rich organic substance which enhances soil characteristics.

1 Q Elite ties [151 9 9 1 1 Stager et a1. Mar. '7, 1972 [54] BIODEGRADABLE CONTAINER 2,858,647 11/1958 Cotton ..47/37 [72] Inventors: Francis W. Stage Robert N. Minor both 3,102,364 9/1963 Pullen ....47/37 of Stafford Springs Conn 2,960,799 11/1960 Schneider ..47/37 3,415,402 12/1968 Webber 215/1 C [73] Assignee: Biocor Corporation, Stafford Springs, 3,198,740 8/1965 Dunlop et al.. .....252/90 COfm- 1,571,447 2/1926 l-luxham ..260/19 R 22 F1 d: l 1970 I 1 I 6 June Primary Examiner-Alfred L. Leavitt PP 42/010 Assistant Examiner-Edward G. Whitby Attorney-Fishman and Van Kirk [52] 11.8. CL ..220/83, 220/D1G. 30, 206/D1G. 34,

229/35 R, 260/14, 260/38, 117/94, 117/95, 117/33, [571 ABSTRACT 1 17/161 99/181 R A container which deteriorates after a l d pro onge exposure to [51] I111. Cl. ..B65d 25/34, 865d 25/14 moisture and Oxygen in an atmospheric environment with the [58] 235 g s 1 220mm: 83; aid of biological agents. The container material has organic y gi g lg components that are nutrients to fungi and various bacteria b which bring about the decomposition. The material is composed of an organic filler material, such as peat, and a phenolic resin impregnated with a metallic salt of a fatty acid. The [56] References Cited decomposition process transforms the container material into UNITED STATES PATENTS a rich organic substance which enhances soil characteristics.

3,467,609 9/ 1969 Adams et a1. ..47/37 X 20 Claims, 2 Drawing Figures PATENTEUMAR 7 I972 INVENTORS FRANCIS W. STAGER ROBERT N. MINOR BYIzmWm/J ATTORNEYS BIODEGRADABLE CONTAINER BACKGROUND OF THE INVENTION:

1. Field of the Invention This invention relates to the field of degradable materials and more particularly to container materials which decompose with the aid of biological agents after prolonged exposure to the atmospheric environment.

2. Description of the Prior Art A problem which is becoming more severe, particularly in heavily populated areas, is the disposal of waste materials. Large quantities of waste material are discarded daily and greatly tax disposal facilities, frequently to the straining point. Land available for dumping of trash and garbage has become more critical as other, more profitable uses for the land evolve. Furthermore, only selected sites may be employed as disposal areas so that the remaining land may be preserved either in a natural state or in a pleasant environment for both business and residential uses.

The burning of litter poses a similar problem to disposal authorities because of ecological considerations. Air pollution around larger cities is a serious problem which is being attacked from many sides. In addition, pollution of other natural bodies such as rivers and streams may convert common items such as swimming and drinking water, currently taken for granted, into scarce resources.

Quite aside from the disposal problem, many natural spots of beauty are defaced daily by thoughtless depositing of litter along roadsides and in public recreation areas and parks. This litter usually consists of bottles and cans made from glass and aluminum which will never decompose. Costly pickup programs of municipal and state highway departments are inaugurated to eliminate such litter.

In conjunction with the foregoing problems, the field of decomposable materials has recently taken on new interest. While the more urgent need for a disposable material has been generated by current problems, disposable materials themselves are not entirely new. US. Pat. No. 2,982,394 discloses a material which decomposes in water. The material is employed for dispensing soil conditioning agents by packaging the agents in the decomposable material and allowing the dampness of the soil to deteriorate the material.

A container which breaks down upon exposure to normal atmospheric conditions is disclosed in US. Pat. No. 3,415,402. This container is composed of selected chemicals which react with one another to dissolve the remaining materials following the breakdown of an outer protective coating.

US. Pat. No. 3,232,865 employs bacterial agents to purify waste water. While this patent is not concerned with decomposable materials, it does pertain to the field of ecology and is of interest with respect to the present invention due to its use of bacterial agents.

While materials which do decompose are known, such materials frequently breakdown by compound changes or interactions of the components themselves. Plastics, for example, breakdown upon exposure to sunlight and other environmental factors. It is accordingly an object of the present invention to disclose a material which decomposes without an interaction of the container materials themselves.

It is an object of the present invention to disclose a material which withstands temporary, although complete, submersion in water, but breaks down after prolonged exposure to water and oxygen.

It is also an object of the present invention to disclose a biodegradable material that breaks down through the aid of fungi and bacterial agents which occur naturally throughout our environment in the presence of oxygen and water.

It is still a further object of the present invention to disclose a compound which forms a rich soil-improving material upon prolonged exposure to natural atmospheric conditions.

SUMMARY OF THE INVENTION The bio-degradable material of the present invention is comprised basically of an organic filler material, a phenolic resin without fungicidal agents and a metallic salt of a fatty acid which forms a bacterial and fungi nutrient. The organic filler material may be peat, wood flour, cotton, linen or other organic material which has a fibrous character that provides structural definition when combined with the phenolic resin. The metallic salt of a fatty acid, such as zinc stearate, calcium stearate or other metallic salts are usually added as stoppers or fixers to the phenolic resin. The salts affect the flow characteristics and add to the knitting and wetting properties of the compound. In excess quantities, the stearates bleed to the surface of the molded structure and form fatty acids on which bacteria and fungi feed. The action of the fungi and bacteria cause the material to decompose and the organic filler enhances the decomposition process by forming a rich organic substance in the process.

The biodegradable composition can be molded in the form of a container. The exterior surface of the container is protected by a thin coat of Iithographed, water-soluble paint and the interior surface, with a coat of plastic, metal flash or wax, commonly used in beverage and food containers. The protective coats temporarily impede the decomposition process until a prolonged exposure to high humidity or water removes the exterior coat. Once the outer protective coat has been broken down, the stearates of the fatty acid bleed to the surface of the core material. The hydrolized stearates and oxidized aldehydes from the phenolic resin form biological nutrients. Fungi and bacteria feeding on the nutrients complete the decomposition process by turning the organic filler material into a healthy soil conditioner.

The composition of the biodegradable material is principally the organic filler material which comprises between -95 percent by volume of the material. The metallic salts of the fatty acid range between 2-6 percent by volume, and the phenol formaldehyde binder or resin which holds the material together forms between 3-8 percent by volume of the material.

The bio-degradable material is made by blending all three components. The precise container structure is formed in a mold and the mixture is poured and pressed into the mold at pressures in-the range of 2,000-6,500 p.s.i. The curing process depends on the particular resin employed and the thickness of the cross section to be cured. Normally, the temperature range lies between 325-425F. The molding time at the curing temperature is brief and in the range of 45-l20 seconds. Mold charge and closing times should be regulated to obtain material densities ranging from 0.75-0.95 g./cc. These densities directly affect moisture absorption rate.

BRIEF DESCRIPTION OF THE DRAWINGS The present invention may be better understood by reference to the accompanying drawings.

FIG. 1 shows a container of the type which may be constructed with the novel biodegradable material.

FIG. 2 is a partial cross-sectional view of the container shown in FIG. 1 as seen along the section line 2-2.

DESCRIPTION OF THE PREFERRED EMBODIMENTS A typical container of the type which would be formed by the novel biodegradable material is shown in FIG. 1. Such container, generally designated 10, may be used for transporting food or beverages in much the same manner as aluminum or tin-coated steel cans are currently employed. The container 10 is molded as described hereinafter and may take any desired shape that can be formed in a mold, such a pure cylindrical form or more fancy rounded, elliptical and irregular forms. The top of the container 12 is sealed to the body 14 to protect the contents of the can under normal dry storage conditions. The seal between the top 12 and the body 14 could be provided by an elastic lip around the periphery of the top 12 or by a fibrous gasket which engages the circular end surfaces of the body 14 in much the same manner as metallic caps are sealed with glass food containers.

The top 12 and the body 14 of the container may be manufactured from the biodegradable material. The container is made from a laminated structure 16 which has an interior protective coat 18, a core 20 formed from the biodegradable material and an exterior protective coat 22.

The interior protective coat 18 separates the contents of the can from the biodegradable material and acts as a protective sealant for the contents. Such material is currently employed in food containers any may take the form of a thin plastic liner, such as polyethylene, a metal flash, such as tin, or a very thin layer of wax. The protective coat 18 may not itself be readily decomposable; however, the coat 18 is extremely thin since it does not perform a significant structural function within the laminated structure 16. Because of its very thin characteristics, normal atmospheric conditions will break down the material with little or no residue.

The exterior protective coat 22 is made for appearance purposes as well as the protective function. The coat 22 may be made from a water-soluble paint which is lithographed onto the external surface of the container after molding. Paints of this type are readily available and in one form are known as water base latex paints. While the paint is water soluble, the paint resists deterioration when exposed to water or humidity for short periods of time. Temporary, although complete, submersion in water will have little residual effect on the containers and prolonged storage in a dry environment will not result in a breakdown of the paint.

The biodegradable core material 20 provides structural rigidity for the laminate structure 16 and any container manufactured from the material. The material is composed of three basic constituents, an organic filler material, a metallic salt of a fatty acid and a binder or resin.

The organic filler material is any fibrous organic material such as peat, wood flour, cotton or linen. Composites of various organic materials may also be employed. The fibrous nature of the organic filler permits the resin to join the various components together in a mixture having sufficient strength to withstand the normal handling expected of food containers. Upon decomposition by the biological agents, the fillers are converted to a rich humus which enhances soil characteristics.

The resin which binds the several components of the degradable material together is an A- or B-type phenol formaldehyde resin of either a single or two-stage variety available from suppliers such as Hooker Chemical Co. The terms singleor two-stage refer to the characteristics of the materials formed. The one stage or resol type phenolic resin can completely polymerize upon heating. The two-stage or novalak resins require additional aldehyde or cross-linking agents such as hexamethylenetetramine to cure when heated. While most phenolic resins that are used in the molding processes today have fungicidal agents added to prevent fungal and bacterial growth, these additives are not employed in the phenolic resin of the present invention. Instead, the growth of bacteria and fungi is encouraged to aid in the decomposition process.

To further encourage the biological decomposition, metallic salts of fatty acids, for example salts from the stearate group such as calcium stearate, cadmium stearate, zinc stearate are added to the resin in excessive amounts. These stearate compounds are normally used in lesser amounts to stop or fix the curing process of the phenolic. By addition of greater amounts of the stearates to the resin, greater amounts of the stearates will bloom on the surface of the core material due to a bleeding effect of the resins. As the stearates come to the surface of the core material, they are hydrolized by emulsifying with water and form fatty acid emulsions characterized by the particular alkyl radical, that is the stearates are converted into stearic acid. The fatty acids may also be formed by the aldehydes in the resin which are oxidized at the surface of the core material. Such fatty acids are the nutrients on which many fungi and bacteria are nourished.

Further additives may be employed to provide a favorable environment for bacterial growth. These additives may include nitrogenous materials such as ammonium nitrate from which the organisms and fungus derive nitrogen. The acidity of the mixture may also be increased by the addition of tannic acid. The increased acidity stimulates the fungus development in the decomposition process. Breakdown of the core material may be accelerated by the addition of aluminum sulfate to the base mixture shortly before it is molded and enclosed with the protective inner and outer coatings.

Since the principal portion of the core material is organic, bacteria and fungi which are nourished by the fatty acids may thrive on the organic material and convert such organic material into a soil-enriching humus after moisture and sunlight have broken away the exterior protective coat 22 and exposed the decomposable core 20. The phenolic resin without a fungicidal agent encourages the growth of biological agents. The cooperative action of the resin and the metallic salt which forms the fatty acid, a biological nutrient, favors the multiplication of biological agents which in turn change the organic matter into a soil-enhancing humus. Two advantages are therefore immediately apparent. The container from which the biodegradable material is formed disappears and also the soil upon which the container lies is enriched.

The formation of the biodegradable container material is accomplished by first mixing the material and then curing the material in a heated mold.

In mixing the biodegradable material, the three principal constituents are first thoroughly mixed in dry form. If the resin is a liquid, the metallic salts of the fatty acids such as stearates are added to the resin in appropriate amounts and the organic filled material in dry form is then blended with the liquid resin.

The range of compositions of the constituents can be varied according to the desired characteristics of the container such as strength, rate of decomposition and manufacturing economy. For example, if the considerations of strength are foremost, the percent or organic filler material will be of principal interest. On the other hand, where the rate of decomposition is the more critical parameter, the quantity of the component which forms the fatty acids will be controlling. In general, the ranges of the constituents would be as follows: the phenolic resin may form between 38 percent by volume of the blended mixture; the metallic salt of the fatty acid would be approximately 2-6 percent by volume of the mixture and the remainder of the material, that is approximately -95 percent by volume, would be organic material with incidental impurities.

Once the blended mixture has been formed, it is placed in a mold having the contours of a particular container. In the case of a pressure molding process, the mixture would be formed at a pressure between 2,000p.s.i.-6,500p.s.i. If the particular resin requires heat for curing, the mold may be provided with a heating jacket or electrical heating coils. The curing temperature varies according to the resin and the particular wall thickness of the part. Normally the phenolic resins are cured in a range between 325-425 F. and the molding time extends between 45-120 seconds. Mold charge and closing times should be regulated to obtain densities in the finished article in the range of 0.75-0.95 gJcc. The density of the article is important because it directly affects the moisture absorption rate from the surrounding environment.

Once the biodegradable material has been molded in the shape of a container, it is then coated internally and externally. Internally, a liner of wax, metal flash, or plastic is applied. it is also possible to suspend a loose liner such as a thin polyethylene sack from the lip of the container. Externally, a thin coating of water soluble paint is applied by standard lithographic processes. The paint improves the appearance of the container and also provides identifying or advertising information. The water solubility of the paint may be varied. Complete although temporary submersion of the container should not allow immediate deterioration of the coating. The solubility of the paint should allow the finished container tobe stored in a low-humidity environment for extended storage periods. It is also feasible that in instances where prolonged storage in a damp environment is contemplated, a more permanent, nonsoluble coating may be applied which nevertheless would deteriorate in a natural atmospheric environment. Such thin coating, while not decomposable, may be satisfactory since the principal portion of the container, the structural core material, is decomposable and very little residue from the coating would be expected.

Tests on specific examples of the novel biodegradable core material have been conducted to determine their suitability and rate of deterioration. A synopsis of a few of the examples tested follows:

EXAMPLE I In this example the core mixture was composed of 5 percent by volume of phenolic A-type resin, 3 percent by volume zinc stearate and the remainder being the organic material, in this case peat. The mixture was formed in a wafer under a molding pressure of approximately 6,500 p.s.i. and held at a mold curing temperature of approximately 375400 F. for 1% minutes. The thickness of the resulting wafer was 0.093 inches.

EXAMPLE [I In this case, a phenolic B type resin was mixed with zinc stearate and peat. The percentages by volume were 3 percent for the resin, 5 percent for the stearate and approximately 90 percent peat. To this mixture a small amount of aluminum sulfate, approximately 2 percent by volume, was added to encourage material break down. Again a molding pressure of 6,500 p.s.i. and mold curing temperatures within the range of 375-400 F. were employed for approximately 1 1% minutes.

EXAMPLE III EXAMPLE IV The composition consisted of approximately 4 percent A- type phenolic resin, 5 percent zinc stearate and 90 percent peat. Tannic acid, approximately 1 percent by volume, was added to increase the acidity of the molded wafer. Molding was accomplished at approximately 6,300 p.s.i. and the curing time was approximately 1 minute.

EXAMPLE V In this example the phenolic B-type resin formed only 2 percent of the mixture while the zinc stearate component was increased to 6 percent. Organic peat formed approximately 85 percent of the material to which an aluminum sulfate additive,

approximately 7 percent by volume, was injected prior to molding according to the same parameters as in Example I.

EXAMPLE VI In this example, the basic organic matter was wood-flour and composed approximately 90 percent of the material.

Phenolic resin A at approximately 3 percent by volume was combined with an equal percentage of a stearate in this instance, calcium stearate rather than zinc stearate. To this mixture ammonium nitrate was added to form approximately 4 percent by volume of the molded material. Again, molding and curing were as described in Example I.

EXAMPLE VII To a mixture of 5 percent by volume phenolic resin B, 2 percent cadmium stearate and percent peat, tannic acid was added to form the balance of the mixture. The molding process was carried out at approximately 6,300 p.s.i. for 1 minute.

In each of the above examples, the core material took the shape of a wafer in its molded state. These wafers were then placed in a dark environment which was held at 60-70 F. The relative humidity of the environment fluctuated between 40 percent and 100 percent. In each case, contamination, that is initial signs of fungus growth, were noted within two weeks which indicated that the decomposition process had indeed begun.

While the novel biodegradable container material has been described in various embodiments above, it should be understood that substitutions and modifications can be made in the examples given. The particular stearates may be replaced by equivalent metallic salts which generate the fatty acids upon which bacteria and fungi thrive. In addition, other organic materials than those disclosed above can provide the necessary fibrous structure which, in combination with the binder, produces the structural strength required of the finished container. The binder itself is a phenolic resin without the fungicidal agent normally added to impede attack by fungi and bacteria. It will, therefore, be understood that, while a number of specific embodiments have been given, the invention has been described by way of illustration rather than limitation.

What is claimed is:

1. A biodegradable container comprising:

an organic filler material providing structural integrity throughout the container;

a metallic salt of a fatty acid intermixed with the organic filler; and

a binding agent joining the organic filler with the intermixed metallic salt of a fatty acid in a rigid container form.

2. The biodegradable container of claim 1 wherein:

the organic filler has fibrous character of the rigid container form. 3.The biodegradable containefiimfim 2 whEFe in; "l the organic filler comprises no more than by volume of the rigid container form. v

iI TlE biodegradable container of claim 1 additionally including;

a water-soluble protective coating covering the outside surface of the container for preserving the container in the absence of a humid environment.

5. The biodegradable container of claim 1 wherein:

the binding agent is a phenol formaldehyde resin essentially free of fungicidal additives.

6. A biodegradable material comprising:

a filler providing structural definition of the material and being an organic substance;

a fatty acid product mixed throughout the filler material, said fatty acid product being capable of hydrolyzing to form a biological nutrient; and

a binder distributed throughout the material joining the fatty acid product and the filler in a unified form.

7. The biodegradable material of claim 6 wherein: the filler is a fibrous organic substance.

8. The biodegradable material of claim 7 wherein: the organic substance is peat.

9. The biodegradable material of claim 6 wherein: the

product is a salt of a fatty acid.

10. The biodegradable material of claim 9 wherein: the salt of a fatty acid is a stearate.

11. The biodegradable material of claim 10 wherein:

the salt is a stearate selected from the group consisting of zinc stearate, calcium stearate and cadmium stearate.

12. The biodegradable material of claim 6 in a molded configuration wherein:

the tiller forms 85-95 percent by volume of the material.

13. The material of claim 12 wherein:

the fatty acid product is a salt of a fatty acid comprising apaluminum sulfate in an amount not substantially exceeding proximately 2-6 percent by volume of the material. 7 percent by volume of the material. 14. The material of claim 13 wherein: 18. The biodegradable material of claim 6 in the form of a the binder is a phenolic resin compfising approximately 8 container including:

percent by volume of the material. a piqttective coating covering the exterior surface of the 15. The biodegradable material of claim 12 additionally iricontainer form. lu ing 19. The biodegradable material of claim 18 wherein:

an organic acid additive. the protective coating is a water-soluble exterior coating. The biodegradable m ri l of im 9 in l ing: 20. The biodegradable material ofclaim 18 including: a nitrogenous fungal nutriem- 10 an additional protective coating extending throughout the 17. the biodegradable material of claim 12 additionally ininterior surface of the Container form. eluding: 

2. The biodegradable container of claim 1 wherein: the organic filler has fibrous character of the rigid container form.
 4. The biodegradable container of claim 1 additionally including; a water-soluble protective coating covering the outside surface of the container for preserving the coNtainer in the absence of a humid environment.
 5. The biodegradable container of claim 1 wherein: the binding agent is a phenol formaldehyde resin essentially free of fungicidal additives.
 6. A biodegradable material comprising: a filler providing structural definition of the material and being an organic substance; a fatty acid product mixed throughout the filler material, said fatty acid product being capable of hydrolyzing to form a biological nutrient; and a binder distributed throughout the material joining the fatty acid product and the filler in a unified form.
 7. The biodegradable material of claim 6 wherein: the filler is a fibrous organic substance.
 8. The biodegradable material of claim 7 wherein: the organic substance is peat.
 9. The biodegradable material of claim 6 wherein: the product is a salt of a fatty acid.
 10. The biodegradable material of claim 9 wherein: the salt of a fatty acid is a stearate.
 11. The biodegradable material of claim 10 wherein: the salt is a stearate selected from the group consisting of zinc stearate, calcium stearate and cadmium stearate.
 12. The biodegradable material of claim 6 in a molded configuration wherein: the filler forms 85-95 percent by volume of the material.
 13. The material of claim 12 wherein: the fatty acid product is a salt of a fatty acid comprising approximately 2-6 percent by volume of the material.
 14. The material of claim 13 wherein: the binder is a phenolic resin comprising approximately 3-8 percent by volume of the material.
 15. The biodegradable material of claim 12 additionally including: an organic acid additive.
 16. The biodegradable material of claim 9 including: a nitrogenous fungal nutrient.
 17. the biodegradable material of claim 12 additionally including: aluminum sulfate in an amount not substantially exceeding 7 percent by volume of the material.
 18. The biodegradable material of claim 6 in the form of a container including: a protective coating covering the exterior surface of the container form.
 19. The biodegradable material of claim 18 wherein: the protective coating is a water-soluble exterior coating.
 20. The biodegradable material of claim 18 including: an additional protective coating extending throughout the interior surface of the container form. 